Manufacture and processing of cold rolled steel - 翻译中...
Cold rolled steel is steel produced by cold rolling. Cold rolling is the further thinning of No.1 steel plate to the desired thickness at room temperature. Compared with hot-rolled steel plate, cold-rolled steel plate thickness is more accurate, and the surface is smooth and beautiful, but also has a variety of superior mechanical properties, especially in terms of processing properties. Because the cold-rolled coil is brittle and hard, it is not suitable for processing, so the cold-rolled steel plate is usually required to be annealed, pickling and surface smoothing before being handed to the customer. The maximum thickness of cold rolling is below 0.1-8.0mm, such as the thickness of most cold-rolled steel plates in factories is below 4.5MM; The minimum thickness and width are determined according to the equipment capacity and market demand of each plant.
Introduction
The difference between cold rolled steel and hot rolled steel is not in the smelting process, but in the rolling temperature, or the rolling end temperature. Cold rolled steel is cold-rolled if the final rolling temperature is lower than the recrystallization temperature of the steel. Hot rolled steel is easy to roll and has high rolling efficiency, but the steel is oxidized under hot rolling conditions, and the surface of the product is dark and gray. Cold rolled steel requires large mill power, low rolling efficiency, and intermediate annealing in order to eliminate work hardening during the rolling process, so the cost is also high, but the surface of cold rolled steel is bright, good quality, and can be directly used to process finished products, so cold rolled steel is widely used.
Processing method
Hot-rolled steel coil is used as raw material, and cold continuous rolling is carried out after pickling to remove the oxide skin, and the finished product is rolled hard coil. Because of the cold hardening caused by continuous cold deformation, the strength and hardness of rolled hard coil increase, and the toughness and plastic index decrease, so the stamping performance will deteriorate, and can only be used for simple deformed parts. Rolled hard coil can be used as raw material in hot dip galvanizing plant, because hot dip galvanizing units are equipped with annealing lines. The rolled hard coil weight is generally 6~13.5 tons, and the steel coil is continuously rolled for hot rolled pickling coil at room temperature. The inner diameter is 610mm.
Nắp chai đóng gói và xu hướng phát triển của chúngJuly 4, 2022Đối mặt với nhiều loại đồ uống và đồ uống có cồn khác nhau trên thị trường, bao bì của chúng từ lâu đã là một điểm nhấn thu hút sự chú ý của mọi người. Thiết kế tinh tế và nút chai độc đáo...view
Kiểm tra hiệu suất của gói vận chuyểnJuly 1, 2022Chuẩn bị trước khi kiểm tra gói vận chuyển 1. Phân Tích môi trường tuần hoàn. Định nghĩa lưu thông: Sau khi Sản phẩm được đóng gói, sản phẩm sẽ tạo thành một gói. Đó là toàn bộ quá trình từ khi rời đi...view
Những Điều Cần Biết sau Lễ Hội Mùa Xuân (1)July 4, 2022Thiết bị bảo vệ cá nhân 1. Mũ bảo hiểm an toàn không bị lão hóa, không hư hỏng, và không có bảo trì và biến đổi nhân tạo. 2. Đội mũ bảo hiểm đúng cách: đội mũ đúng cách và đội mũ chắc chắn. 3. WEA...view
Dự đoán tuần sau giá thépJuly 1, 2022Nhìn chung, Giá thị trường thép trong nước tuần này nói chung là một cú sốc mạnh. Trước hết, từ phía cung, trong ngắn hạn Dưới ảnh hưởng của các yếu tố vĩ mô không thể xuất hiện rõ ràng...view